Rapid Injection Molding Polyester TPU Material Manufacturer

Rapid Injection Molding Polyester TPU Material

Request a Quote

View All: http://tpu-material.com/1-2-rapid-injection-molding-polyester-tpu/index.html

The rapid injection molding polyester TPU material is known for distinguished flowability and environmental performance. It features an easy stripping, rapid forming and more advantageous features. Typical applications can be found in gardening shoes, women's soles, shoe accessories, women’s shoe top lifts and other fields.

Product Parameters

Product series Huafon TPU 11 series
Hardness: shore A70—shore D63
Operation: Injection molding
Characteristics: Superior flowability, easy stripping and rapid forming performance
Main models: 1170AP, 1173AP, 1175AP, 1180AP, 1185AP, 1185A, 1190A, 2060D

Technical Specifications

HF-1170AP Polyester Rapid Injection Molding Thermoplastic Polyurethane

Item	Hardness	Tensile strength	Elongation	Tear strength	100% modulus	Abrasion resistance
Test standard	ASTM D2240	ASTM D412	ASTM D412	ASTM D624	ASTM D412	ASTMD5963 Method B rotation method
Unit	Shore A/D	MPa	%	KN/m	MPa	mm ³
HF-1170AP	72A	20	1100	90	3	/

HF-1173AP Polyester Rapid Injection Molding Thermoplastic Polyurethane

Item	Hardness	Tensile strength	Elongation	Tear strength	100% modulus	Abrasion resistance
Test standard	ASTM D2240	ASTM D412	ASTM D412	ASTM D624	ASTM D412	ASTMD5963 Method B rotation method
Unit	Shore A/D	MPa	%	KN/m	MPa	mm ³
HF-1173AP	75A	15	700	80	4	/

HF-1175AP Polyester Rapid Injection Molding Thermoplastic Polyurethane

Item	Hardness	Tensile strength	Elongation	Tear strength	100% modulus	Abrasion resistance
Test standard	ASTM D2240	ASTM D412	ASTM D412	ASTM D624	ASTM D412	ASTMD5963 Method B rotation method
Unit	Shore A/D	MPa	%	KN/m	MPa	mm ³
HF-1175AP	78A	16	700	90	5	/

HF-1180AP Polyester Rapid Injection Molding Thermoplastic Polyurethane

Item	Hardness	Tensile strength	Elongation	Tear strength	100% modulus	Abrasion resistance
Test standard	ASTM D2240	ASTM D412	ASTM D412	ASTM D624	ASTM D412	ASTMD5963 Method B rotation method
Unit	Shore A/D	MPa	%	KN/m	MPa	mm ³
HF-1180AP	80A	16	600	90	5	/

HF-1185A Polyester Rapid Injection Molding Thermoplastic Polyurethane

Item	Hardness	Tensile strength	Elongation	Tear strength	100% modulus	Abrasion resistance
Test standard	ASTM D2240	ASTM D412	ASTM D412	ASTM D624	ASTM D412	ASTMD5963 Method B rotation method
Unit	Shore A/D	MPa	%	KN/m	MPa	mm ³
HF-1185A	85A	18	600	95	6	/

HF-1190A Polyester Rapid Injection Molding Thermoplastic Polyurethane

Item	Hardness	Tensile strength	Elongation	Tear strength	100% modulus	Abrasion resistance
Test standard	ASTM D2240	ASTM D412	ASTM D412	ASTM D624	ASTM D412	ASTMD5963 Method B rotation method
Unit	Shore A/D	MPa	%	KN/m	MPa	mm ³
HF-1190A	91A	35	700	150	9	/

HF-1195A Polyester Rapid Injection Molding Thermoplastic Polyurethane

Item	Hardness	Tensile strength	Elongation	Tear strength	100% modulus	Abrasion resistance
Test standard	ASTM D2240	ASTM D412	ASTM D412	ASTM D624	ASTM D412	ASTMD5963 Method B rotation method
Unit	Shore A/D	MPa	%	KN/m	MPa	mm ³
HF-1195A	95A	36	450	180	15	/

HF-2060DS Polyester Rapid Injection Molding Thermoplastic Polyurethane

Item	Hardness	Tensile strength	Elongation	Tear strength	100% modulus	Abrasion resistance
Test standard	ASTM D2240	ASTM D412	ASTM D412	ASTM D624	ASTM D412	ASTMD5963 Method B rotation method
Unit	Shore A/D	MPa	%	KN/m	MPa	mm ³
HF-2060DS	63D	45	400	210	22	70