Semi-Rigid Heat Shrink Tubing
Request a Quote
Model: CHANGBAO-301
Material: Irradiated cross-linked modified polyolefin
Shrink ratio: 2:1
Applications
The non-flame retardant semi-rigid heat shrink tubing is a zero halogen tubing that is certified to RoHS, REACH and SONY standards. It is a semi-rigid glossy tubing, and features an excellent insulation performance, solvent resistance, diesel resistance and friction resistance. This allows the heat shrink tubing to be used in electronic, automotive and aerospace fields, as well as wire shielding for automotive fuel tubing and refrigeration tubing.
| Size | As supplied (mm) | After recovery (mm) | ||
| Inside diameter (D) | Wall thickness (T) | Inside diameter (d) | Wall thickness (t) | |
| Ф1.0 | 1.5 0.2/-0.1 | 0.18±0.05 | ≤0.60 | 0.36±0.08 |
| Ф1.5 | 2.1 0.2/-0.1 | 0.18±0.05 | ≤0.80 | 0.36±0.08 |
| Ф2.0 | 2.5 0.2/-0.1 | 0.20±0.05 | ≤1.00 | 0.42±0.08 |
| Ф2.5 | 3.0 0.2/-0.1 | 0.22±0.05 | ≤1.25 | 0.46±0.08 |
| Ф3.0 | 3.5 0.2/-0.1 | 0.22±0.05 | ≤1.50 | 0.46±0.08 |
| Ф3.5 | 4.0 0.2/-0.1 | 0.22±0.05 | ≤1.75 | 0.46±0.08 |
| Ф4.0 | 4.6 0.2/-0.1 | 0.22±0.05 | ≤2.00 | 0.46±0.08 |
| Ф4.5 | 5.0 0.2/-0.1 | 0.23±0.05 | ≤2.25 | 0.46±0.08 |
| Ф5.0 | 5.5 0.2/-0.1 | 0.25±0.05 | ≤2.50 | 0.50±0.08 |
| Ф6.0 | 6.5 0.2/-0.1 | 0.25±0.05 | ≤3.00 | 0.55±0.10 |
| Ф7.0 | 7.5 0.2/-0.1 | 0.25±0.05 | ≤3.50 | 0.55±0.10 |
| Ф8.0 | 8.5 0.3/-0.1 | 0.28±0.06 | ≤4.00 | 0.58±0.10 |
| Ф9.0 | 9.5 0.2/-0.1 | 0.28±0.06 | ≤4.50 | 0.58±0.10 |
| Ф10 | 10.5 0.3/-0.1 | 0.28±0.06 | ≤5.00 | 0.58±0.10 |
| Ф11 | 11.5 0.3/-0.1 | 0.28±0.06 | ≤5.50 | 0.58±0.10 |
| Ф12 | 12.5 0.3/-0.1 | 0.28±0.06 | ≤6.00 | 0.58±0.10 |
| Ф13 | 13.5 0.3/-0.1 | 0.28±0.06 | ≤6.50 | 0.58±0.10 |
| Ф14 | 14.5 0.3/-0.1 | 0.28±0.06 | ≤7.00 | 0.58±0.10 |
| Ф15 | 15.5 0.3/-0.1 | 0.28±0.06 | ≤7.50 | 0.58±0.10 |
| Ф16 | 16.5 0.3/-0.1 | 0.28±0.06 | ≤8.00 | 0.58±0.10 |
| Ф18 | 18.5 0.3/-0.1 | 0.32±0.08 | ≤9.00 | 0.68±0.10 |
| Ф20 | 20.6 0.5/-0.2 | 0.32±0.08 | ≤10.0 | 0.68±0.10 |
| Ф22 | 22.6 0.7/-0.2 | 0.35±0.08 | ≤11.0 | 0.72±0.12 |
| Ф25 | 25.6 0.7/-0.2 | 0.40±0.10 | ≤12.5 | 0.78±0.12 |
| Ф28 | 28.6 0.7/-0.2 | 0.40±0.10 | ≤14.0 | 0.78±0.12 |
| Ф30 | 30.6 0.7/-0.2 | 0.40±0.10 | ≤15.0 | 0.82±0.12 |
| Item | Specifications | |
| Shrink temperature (℃) | 120-150 | |
| UL operation temperature (℃) | 105 | |
| Operating temperature (℃) | -40℃-105℃ | |
| Radial shrinkage (%) | ≥50 | |
| Longitudinal shrinkage(%) | ≤±5 | |
| Tensile strength (MPa) | ≥10.4 | |
| Elongation at break (%) | ≥200 | |
| Aging in circulating-air oven | 136.0±1.0℃, 168hrs | |
| After aging | Tensile strength (MPa) | ≥7.3 |
| Elongation at break (%) | ≥100 | |
| UL operation voltage (V) | 600 | |
| Volume resistivity (Ω·cm) | ≥1015 | |
| Dielectric strength (kV/mm) | ≥25 | |
| Concentricity (%) | ≥65 | |